Technological project identification result of Zhejiang SAT(Zhejiang technology identify character[2005]NO.039)invention patent |
Arc Spraying Solid Line
Anti-high temperature corrosion and oxidation solid line series
Serial number |
Wire name |
Major
components |
Coating’s performances |
Application domains |
CL-101 |
CL-NiCrTi(45CT) |
Ni、Cr、Ti |
Compact Coating, well-proportioned organization, high temperature oxidation and Sulfur corrosion capacity, combining intensity ≥40MPa, hardness ≥HRC38, use temperature reaches 1400℃. |
Boiler’s water screen wall, high temperature superheater, and high temperature reheater’s sulfur corrosion-resistant and high-temperature oxidation, smelting, chemical equipment’s high-temperature gas corrosion. It is not necessarily to render. |
CL-102 |
CL-NiCr |
Ni、Cr |
Good high temperature oxidation and corrosion resistant, well-proportioned organization, combining intensity ≥40MPa, hardness ≥HRC32, use temperature 1400℃. |
Boiler’s water screen wall, superheater where needs high temperature oxidation and corrosion, anti-oxidation and corrosion in pressure vessel. It can be used as rendering material. |
CL-103 |
CL-NiCrAl |
Ni、Cr、Al |
Fine coating, good high temperature oxidation and corrosion, high temperature stability, combining intensity ≥45Mpa,hardness ≥HRC35, use temperature 1200℃. |
Boiler’s water screen wall, superheater where needs high temperature oxidation and corrosion, electro thermal working surface protection. It can be used as rendering material of high temperature spraying. |
CL-104 |
CL-FeCrAl |
Cr、Al、Fe |
Good middle and high temperature oxidation performance, General sulphur corrosion resistant capacity, large coating brittleness, hardness ≥HRC38, use temperature 900℃. |
Boiler’s middle heated surface where needs anti-oxidation protection, smelting, chemical equipment’s anti-thermal and oxidation protection.
|
CL-105 |
CL-304 |
Cr、Ni、Ti、Fe |
Austenite base, bigger coefficient of expansion, stronger high-temperature oxidation capability, good tenacity, low hardness, use temperature 800℃. |
Anti-oxidation protection of workpiece which runs under middle temperature, smelting, chemical equipment’s surface protection or repairing of mechanical roller, axis part. |
CL-106 |
CL-316 |
Cr、Ni、Ti、Fe |
Austenite base, bigger coefficient of expansion, stronger high-temperature oxidation capability, good tenacity, low hardness, use temperature 1000℃. |
Boiler’s high-heating surface where needs oxidation protection, smelting equipment, chemical hold tank’s anti-oxidation and heating or surface repairing of roller, axis. |
Anti-abrasion solid line series
CL-201 |
CL-1Cr13 |
Cr、C、Ni、Mo、V、Mn、Fe |
Ferrite base, some of anti-middle temperature oxidation capacity, good coating tenacity, low hardness, hardness ≥HRC30, use temperature 700℃. |
Plain journal bearing, roller’s surface restoration, the restoration of the cast iron piece’s size. |
CL-202 |
CL-2Cr13 |
Cr、C、Ni、Mo、V、Mn、Fe |
Ferrite base, some of anti-middle temperature oxidation capacity, good arrange in pairs of coating tenacity and hardness, hardness ≥HRC35, use temperature 700℃. |
Axle, bearing guard, roller’s surface repairing, anti-oxidation protection of boiler’s middle-heating surface. |
CL-203 |
CL-3Cr13 |
Cr、C、Ni、Mo、Mn、V、Fe |
Ferrite base, some of anti-middle temperature oxidation capacity, worse coating tenacity, better wear resistance, hardness ≥HRC38, use temperature 700℃. |
Surface repairing of mold, gear, axle, roller, valve, metallurgical, chemical, cement equipment where needs anti-middle temperature oxidation and abrasion, anti-oxidation and abrasion on boiler’s middle-heating surface. |
CL-204 |
CL-4Cr13 |
Cr、C、Ni、Mo、V、Mn、Fe |
Ferrite base, some of anti-middle temperature oxidation capacity, better wear resistance, larger coating brittleness, hardness ≥HRC42, use temperature 700℃. |
Surface repairing of cylinder liner, plunger, screw, mold, friction part, etc., metallurgical, chemical, cement equipment where needs anti-middle temperature oxidation and abrasion, anti-oxidation and abrasion on boiler’s middle-heating surface. |
CL-205 |
CL-60SiMn |
C、Mn、Si、Cr、Fe |
Stable anti-middle and low temperature abrasion, good wear resistance, larger coating brittleness, hardness ≥HRC45. |
Surface repairing of cylinder liner, plunger, mold, axis, valve seat, scraper, etc., metallurgical, chemical, cement equipment where needs anti-normal temperature abrasion, protection. |
CL-206 |
CL-50CrV |
C、Cr、V、Si、Mn、Fe |
Stable anti-middle and low temperature abrasion, good wear resistance, some of tenacity, hardness ≥HRC45. |
Surface repairing of cam, cell guide, guide rail, crankshaft, valve, piston, mold, axle, etc., metallurgical, chemical, cement equipment where needs anti-middle and low temperature abrasion, protection. |
Grounding series
CL-301 |
CL-NiAl |
Ni、Al |
Exothermic reaction, micro-metallurgical combining, homogeneous organizations, strong anti-oxidation and corrosion ability, combining intensity ≥60Mpa, use temperature 1000℃. |
High temperature grounding material |
CL-302 |
CL-NiAlTi |
Ni、Al、Ti |
Strong exothermic reaction, good junction plane micro-infiltrate effect, micro-metallurgical combining, strong anti-oxidation and corrosion ability, stable high temperature performance, combining intensity ≥70Mpa, use temperature 1200℃. |
High temperature grounding material. Suitable for any metal or metal-ceramic base workpiece’s rendering |
Non-ferrous metal solid line series
CL-401 |
CL-Al |
Al |
Anti-atmospheric, water, aquafortis, nitrates, organic medium corrosion, good conductive, electric performance. |
Bridge, ship, petrochemical facility framework’s corrosion resistant, but also for the use of high-temperature surface layer of protective coating, ornamental coating. |
CL-402 |
CL-AlZn |
Al、Zn、Mg |
Stress corrosion resistance, good thermal deformation, high intensity, spraying layer is fine |
Vehicle, vessel, transmission tower, steel, bridge’s corrosion resistant |
CL-403 |
CL-AlSi |
Al、Si、Mg |
Good plasticity, atmospheric corrosion resistance, oxidation repaint |
Structural equipment, vehicles, vessels and aluminum, zinc, organic materials’ final protective layer or surface wear-resisting layer |
CL-404 |
CL-Cu |
Cu |
Good conductive, electrothermal performance, good ductility, tolerant atmosphere, organic acid, alkaline, salt corrosion, adsorption ink is good |
Printers, the printing machine doctor’s surface, surface conductive parts, heat conduction layer, corrosion-resistant layer |
CL-405 |
CL-CuZn |
Cu、Zn |
Good conductive, electrothermal performance, good atmosphere, salt spray corrosion resistant, the coating is fine, high hardness. |
Part surface conductive, heat conduction layer and corrosion protection layer, ornamental coating |
CL-406 |
CL-CuNiAl |
Cu、Ni、Al |
Better conductive, electrothermal performance, good abrasion and corrosion resistance, strong heat resistant performance |
Parts surface conductive, heat conduction layer, wear-resisting, corrosion-resisting layer |
CL-407 |
CL-Zn |
Zn |
Low melting point, easy to spraying, dry atmospheric corrosion resistance, it can be used as anode coatings to protect base metal |
Protective coating of more important metal components in the atmosphere or water | |